природа металла) анодно-катодно-омический контроль может переходить в преимущественно анодный, преимущественно катодный или омический. (From www.okorrozii.com).
8 . Work in pairs. Interpret the following passage sentence by sentence.
The most common characteristic of metallic atmospheric corrosion is the localized character of its nucleation. Preferential nucleation sites depend on the metal structure and are associated to the presence of different phases or environmental pollutants on discrete areas of the metallic surface. In the case of carbon steel, nucleation starts with the formation of small protuberances of corrosion products at isolated points on the metallic surface, followed by the formation of a large number of corrosion product nuclei that can cover the entire surface after relatively short exposure times.
9 . Give English equivalents to the following word combinations and learn them by heart:
скорость коррозии
коррозийный процесс
сырость внешних конструкций
коррозия в металлах
химическая активность углеродной стали
атмосферная коррозия меди
агрессивные среды
анодный процесс
прогнозируемость атмосферной коррозии
10 . Give Russian equivalents to the following word combinations and learn them by heart:
galvanic couple
ohmic control
cathodic process
electric conductivity
atmospheric pollution
fossil fuels
combustion products
metal surface
oxide film
11 . Translate the following sentences into Russian.
1. Predictability of atmospheric corrosion, in principle, should be based upon the complete understanding of the corrosion process and interdependence of the contributing parameters.
2. Grossman has investigated the atmospheric factors which determined the time of wetness of the outdoor structures.
3. In polluted atmospheres, chlorides and SO2 are the common pollutants influencing metallic corrosion.
4. Among the factors affecting the type and amount of atmospheric corrosion products, the main role is played by the reactivity of carbon steel.
5. The general sequence of atmospheric corrosion of copper is well known.
6. Atmospheric corrosion can be classified into dry, damp and wet categories.
7. Principal corrosives consist of moisture, relatively small amounts of sulfur oxides, and carbon dioxide from various combustion products.
8. The most potent causes of corrosion in industrial environments are the sulfur oxides and nitrogen oxides produced by the burning of automotive fuels and fossil fuels in power stations.
9. The critical relative humidity, above which metals corrode, drops to about 60 percent when these airborne pollutants are deposited on the metal surface.
10. A fundamental requirement for electrochemical corrosion processes is the presence of an electrolyte.
12 . Translate the following sentences into English.
1. Скорость коррозии и вид коррозионного разрушения зависят от природы металла, влажности, загрязненности атмосферы.
2. Загрязнение атмосферы газами, пылью резко ускоряет коррозию.
3. При образовании фазовых пленок в области мокрой коррозии затруднятся доставка кислорода и наблюдается катодное торможение процесса.
4. Стойкость металлов к атмосферной коррозии зависит от их химической природы и состояния поверхности.
5. Наличие узких щелей и зазоров, в которых возможны капиллярная конденсация и застой влаги, усугубляют атмосферную коррозию и могут привести к образованию коррозионных язв.
6. При относительной влажности, близкой к 100 %, или при непосредственном увлажнении металла (дождь, туман) на поверхности происходит образование видимых фазовых слоев воды.
7. Рост оксидной пленки происходит в первые секунды и минуты.
8. Предельная толщина пленок на железе 30-40 А, на нержавеющих сталях – 10-20 А.
9. Анодный процесс осложняется тем, что продукты коррозии экранируют поверхность металла.
10. Загрязнение атмосферы газами, пылью резко ускоряет коррозию. Это явление наблюдают в промышленных центрах, особенно в присутствии в воздухе SO2, NH3, H2S,C12, HCl.
13 . Translate the following word combinations.
Anodic process – продукты коррозии – industrial cluster – оксидная пленка – oxygen depolarization – продукты горения – wind velocity – корродирующий металл – sulphur oxide – функции ущерба – corrosive surface – экранировать поверхность металла – chemical nature – оксидная пленка